CHARACTERISTICSHADALAN
® V31 13E is a transparent, water-dilutable primer on an epoxy resin base.
As a protective coat, it has good resistance to oil, grease, petrol, diesel and aqueous salt solutions.
- Solvent-free
- Water-dilutable
- Consolidating
- Transparent
- Good resistance
- Fast-reacting
INGREDIENTSEpoxy resin dispersion
USEHADALAN
® V31 13E as sealing and priming for all absorbent, mineral substrates.
As a bonding agent for the subsequent epoxy resin coats.
Areas of application:
- Absorbent mineral substrates
- Ceramic linings
- Primer coating in the system
QUANTITY REQUIREDPrimer
Top coat | 0.1 to 0.2 kg/m2
0.2 to 0.3 kg/m2 |
1) At +20 ℃ and 60 % relative atmospheric humidity.
2) N. Taber: Roll CS 10/1000 U/ 1000 g
PREPARATION OF THE SURFACEThe substrate must be firm, dry, clean, free from dust, absorbent, resilient, and free from release agents, corrosive components or other layers interfering with bonding. The substrate must be generally suitable for the coating system. The adhesive tensile strength of the surfaces should not fall short of 1.5 N/mm². The substrate moisture of cement substrates should not fall short of < 4.0 parts by weight, anhydrite screeds: < 0-5 part by weight.
The compression strength of the substrate must be at least 25 N/mm².
The substrate must be protected from increasing and penetrating moisture. The floor surface has to be prepared by e.g. dust-free shot-blasting, diamond grinding, grinding or other suitable measures. The granular structure must be laid open and all separating substances and loose components must be removed consequently.
As a rule, substrates into whose surface agents (e.g. wax) have been incorporated for smoothing, must be removed by milling and subsequent shot-blasting. Check the compatibility with existing coatings; completely remove layers and coatings without load-bearing capacity. Screeds containing asphalt are difficult substrates due to their formability under mechanical and thermal load. Thus, they may be coated with special systems only. Please contact our technical service department.
Remove the surface of existing tiling being stuck by diamond grinding or milling. The glaze must be removed completely.
All substrate preparations have to be carried out by suitable specialist firms.
APPLICATION | 1. | Mix component A and component B homogeneously with one another.
Mixing ratio:
3 parts by weight of component A : 1 part by weight |
| 2. | Then, dilute the mass with water in a neutral barrel and once again mix thoroughly.
Mixing ratio:
As bonding agent and primer: 1 : 1 part by weight.
As a protective paint, pore closer and under epoxy resin dispersion coatings (HADALAN® LF 41 12E/ HADALAN® EBG 13E/ HADALAN® FGM003 57M), only 25% by weight of water is added. |
| 3. | The coat is applied with a brush, rubber wiper or roller. To achieve uniform surfaces, the coating is applied with a suitable short-fibre roller for epoxy resins. The coat is applied cross-wise. |
| 4. | Clean all processing equipment with water immediately after use. |
IMPORTANT NOTES- Maintain the processing temperature of +5 ℃ to +35 ℃.
- High temperatures accelerate, low temperatures delay the hardening process.
- High atmospheric humidity as well as increased substrate wetness delay the hardening process.
- Ensure good drying conditions in the interior.
- Irregular material coatings and/or bad ventilation during the drying phase can result in differences in the colour shade and gloss.
- The substrate temperature must be at least 3 °C above the dew point temperature.
SAFETY PROVISIONS/RECOMMENDATIONSInformation regarding the safety during transport, stor- age and handling are included in the updated safety data sheets.
Detailed instructions can be obtained from the code of practice “Epoxy resins in the building industry“, published by the Arbeitsgemeinschaft der Bau-Berufsgenossenschaften (study group of the professional construction guilds). Tiefbau-Berufsgenossenschaft (underground construction guild), Industrieverband Klebstoffe e.V. (industrial association of adhesives), and Holzschutzmittel e.V. (association of wood protection agents) in Frankfurt.
DISPOSALThe local waste removal regulations must be observed.
SPECIFICATIONSPackaging
Combination barrels
Component A
Component B
Delivery form
Colour shade
Processing temperature
Processing time1)
Optimum coating interval
Walkable1)
Capably of being mechanically
fully loaded
Capable of being chemically
fully loaded
Surface tensile strength
Abrasion loss2)
Storage | Tin bucket
4 kg
3 kg
1 kg
56 barrels/pallet
transparent
+5 ℃ to +35 ℃
approx. 60 minutes
between 1.5 and 24 hours
after approx. 3 hours
after 3 days
after 5 days
> 1.5 N/mm2
0.031 g
frost-free, 12 months |